ESTIMATING THERMAL STABILITY OF PHOSPHATED AND PHOSPHATED SULFATED MESOPOROUS ZIRCONIA
Keywords:mesoporous, zirconia, oxophosphate, thermal stability
Mesoporous phosphated zirconia (m-PZ) and mesoporous phosphated sulfated zirconia (m-PSZ) were synthesized through condensation methods using Zr3(PO4)4 and Zr(SO4)2 as precursors respectively. The precursors, solvents with suitable molar or mass ratios were mixed at 100oC for 48 hours to obtain the mesoporous channels. An oxophosphate process was used to synthesize the m-PSZ material for improving its thermal stability. Some techniques was used to characterize the materials such as SAXRD, TG-DTA and TEM.
Authors who publish with Vietnam Journal of Science and Technology agree with the following terms:
- The manuscript is not under consideration for publication elsewhere. When a manuscript is accepted for publication, the author agrees to automatic transfer of the copyright to the editorial office.
- The manuscript should not be published elsewhere in any language without the consent of the copyright holders. Authors have the right to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal’s published version of their work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are encouraged to post their work online (e.g., in institutional repositories or on their websites) prior to or during the submission process, as it can lead to productive exchanges or/and greater number of citation to the to-be-published work (See The Effect of Open Access).