2K/UV dual-curable acrylate epoxy/SiO2 nanocomposite coatings: crosslinking and mechanical properties
Author affiliations
DOI:
https://doi.org/10.15625/2525-2518/17254Keywords:
acrylate epoxy, polyisocyanate, SiO2 nanoparticles, mechanical properties, 2K/UV dual-cure coatingAbstract
This work aimed to enhance the adhesion of photocurable acrylate epoxy/SiO2 nanocomposite coating by adding a crosslinking agent polyisocyanate Desmodur N75 (N75) to make a 2K/UV dual-curable paint formulation. The obtained results showed that the presence of the curing agent N75 slightly reduced the conversion efficiency of acrylate groups during the UV curing process. The analysis of mechanical properties indicated that the coating achieved the optimal mechanical properties at the N75 content of 5 wt.%. The gel fraction, swelling degree, adhesion to wood and steel, relative hardness, impact resistance, and abrasion resistance reached 97.22 %, 310.05 %, 0.1, 0.94, 90 Kg.cm, and 178 L/mil, respectively. FESEM analysis showed that the paint film was fairly homogeneous and tightly structured. The reactions of components of BGDM, HDDA, I184, N75 and nano-SiO2 in the 2K/UV dual-curable acrylate epoxy/SiO2 nanocomposite coatings were described.
Downloads
References
Nguyen-Tri P., Nguyen T. V. - Radically curable nanobased coatings (chapter 10), In: Phuong Nguyen Tri, Sami Rtimi and Claudiane Ouellet-Plamondon (Eds), Nanomaterials Based Coatings, Elsevier, 2019, pp. 1-35. https://doi.org/10.1016/B978-0-12-815884-5.00010-7.
Nguyen T. V., Nguyet H. M., Linh D. T. M. - Influence of organic UV absorber on the accelerated weathering stability of UV curing coating based on acrylate urethane resin, Vietnam J. Chem. 58 (2) (2020) 173-179. https://doi.org/10.1002/vjch.201900127.
Le X. H., Nguyen T. V., Le M. T., Nguyen T. V. Trieu - Study of photocrosslinking reaction of the resin system on the base of copolymer of tung and soyabean oils, methyl methacrylate, styrene, Vietnam J. Sci. Tech. 48 (3A) (2010) 150-157.
Nguyen N. L., Dang T. M. L., Nguyen T. A., Ha H. T., Nguyen T. V.- Study on Microstructure and Properties of the UV Curing Acrylic Epoxy/SiO2 Nanocomposite Coating. Journal of Nanomaterials, 2021.https://doi.org/10.1155/2021/8493201.
Do T. V., Ha M. N., Nguyen T. A., Ha H. T., Nguyen T. V. - Crosslinking, Mechanical Properties, and Antimicrobial Activity of Photocurable Diacrylate Urethane/ZnO-Ag Nanocomposite Coating, Adsorption Science & Technology, 2021. https://doi.org/ 10.1155/2021/7387160.
Brito M. de, Allonas X., Croutxé-Barghorn C., Palmieri M., Alig I. - Kinetic study of photoinduced quasi-simultaneous interpenetrating polymer networks, Progress in Organic Coatings 73 (2 - 3) (2012) 186-193. https://doi.org/10.1016/j.porgcoat.2011.10.014.
Talita A. T. C., Aline de A. N., Ingrid K. B. dos S., Amanda R. P. de R., Eduardo M. da S. - Characterization of low-shrinkage dental composites containing methacrylethyl-polyhedral oligomeric silsesquioxane (ME-POSS), Journal of the Mechanical Behavior of Biomedical Materials 90 (2019) 566-574. . https://doi.org/10.1016/j.jmbbm.2018.10.028.
Lee S. J., Kawashima S., Kim K. J., Woo S. K., Won J. P. - Shrinkage characteristics and strength recovery of nanomaterials-cement composites, Composite Structures 202 (2018) 559-565. https://doi.org/10.1016/j.compstruct.2018.03.003.
Tafesse M., Kim H. K. - The role of carbon nanotube on hydration kinetics and shrinkage of cement composite, Composites Part B: Engineering 169 (2019) 55-64. https://doi.org/10.1016/j.compositesb.2019.04.004.
Bhanu P., Ravi K. G., Bhuvnesh B., Meetu N. - Modeling based experimental investigation on polymerization shrinkage and micro-hardness of nano alumina filled resin based dental material, Journal of the Mechanical Behavior of Biomedical Materials 99 (2019) 86-92. https://doi.org/10.1016/j.jmbbm.2019.06.026.
M. Sangermano, W. Carbonaro, G. Malucelli, A. Priola, UV‐Cured Interpenetrating Acrylic Epoxy Polymer Networks: Preparation and Characterization, Macromol. Mater. Eng. 93 (2008), 515-520. https://doi.org/10.1002/mame.200800020.
Rocco C., Karasu F., Croutxé-Barghorn C., Allonas X., With de G. - Highly-interpenetrated and phase-separated UV-cured interpenetrating methacrylate–epoxide polymer networks: Influence of the composition on properties and microstructure, Materials Today Communications 6 (2016) 17-27. https://doi.org/10.1016/j.mtcomm.2015.11.004.
Sufyan G., Pekka K. V., David C. W., Lippo V. J. L. - Effect of nanofiller fractions and temperature on polymerization shrinkage on glass fiber reinforced filling material, Dental Materials 24 (5) (2008) 606-610. https://doi.org/10.1016/j.dental.2007.06.020.
Lee S. J., Kawashima S., Kim K. J., Woo S. K., Won J. P. - Shrinkage characteristics and strength recovery of nanomaterials-cement composites, Composite Structures 202 (2018) 559-565. https://doi.org/10.1016/j.compstruct.2018.03.003.
Le T. T., Nguyen T. V., Nguyen T. A., Nguyen T. T. H., Hoang T., Tran D. L., Dinh D. A., Nguyen T. M., Le T. L. - Thermal, mechanical and antibacterial properties of water-based acrylic polymer/SiO2-Ag nanocomposite coating, J. Mater. Chem. Phys. 232 (2019) 362-366. https://doi.org/10.1016/j.matchemphys.2019.05.001.
Nguyen T. V., Nguyen T. A., Nguyen T. H. - The Synergistic Effects of SiO2 Nanoparticles and Organic Photostabilizers for Enhanced Weathering Resistance of Acrylic Polyurethane Coating, J. Compos. Sci. 4 (2020) 23.https://doi.org/10.3390/ jcs4010023.
Bui T. M. A., Nguyen T. V., Nguyen T. M., Hoang T. H., Nguyen T. T. H., Lai T. H., Tran T. N., Nguyen V. H., Hoang V. H., Le T. L., Tran D. L., Dang T. C., Vu Q. T., Nguyen T. P. - Crosslinking mechanism, mechanical properties and weathering degradation of acrylic polyurethane nanocomposite coating reinforced by SiO2 nanoparticles issued from rice husk ash, J. Mater. Chem. Phys. 241 (2020) 122445. https://doi.org/10.1016/j.matchemphys.2019.122445.
Nguyen T. M., Bui T. M. A., Nguyen T. V. - Acid and alkali resistance of Acrylic polyurethane/R-SiO2, Vietnam Journal of Chemistry 58 (1) (2020) 67-73. https://doi.org/ 10.1002/vjch.2019000124.
Hoang T. H. T., Hoang T. H., Nguyen T. V., NguyenT. A.- The Alkaline Resistance of Waterborne Acrylic Polymer/SiO2 Nanocomposite Coatings. Journal of Analytical Methods in Chemistry, 2022.https://doi.org/10.1155/2022/8266576.
Nguyen T. V., Nguyen T. P., Sohrab A., Tran C. D., Hoang D. M., Hoang T. H., Nguyen T. L., Bui T. T. L., Dam X. T., Nguyen N. L., Le T. T., Nguyen T. N. L., Vu Q. T., Tran D. L., Dinh D. A., Le T. L. - The role of organic and inorganic UV-absorbents on photopolymerization and mechanical properties of acrylate-urethane coating, Mater. Today Commun. 22 (2020) 100780.https://doi.org/10.1016/j.mtcomm.2019.100780.
Yari H., Moradian S., Tahmasebi N. - The weathering performance of acrylic melamine automotive clearcoats containing hydrophobic nanosilica, J. Coat. Technol. Res. 11 (2013) 351-360.DOI:10.1007/s11998-013-9541-z.
Tadele D. M., Zhang C., Liu Y., Diaa E. D. F., Yanli Z. - Surface modification of nano-silica by diisocyanates and their application in polyimide matrix for enhanced mechanical, thermal and water proof properties. Materials Chemistry and Physics 225 (2019) 358-364. https://doi.org/10.1016/j.matchemphys.2018.12.107.
Toker R. D., Kayaman A. N., Kahraman M. V. - UV-curable nano-silver containing polyurethane based organic–inorganic hybrid coatings.Progress in Organic Coatings 76 (2013) 1243-1250. https://doi.org/10.1016/j.porgcoat.2013.03.023.
Arndt L. W., Junker L. J., Patel S. P., Pourreau D. B., Wang W. - UV-Curable Acrylic Urethane Coatings for Weatherable Applications, Paint án Coatings Industry, 2004.
Nguyen T. V., Le X. H., Dao P. H., Decker C., Nguyen T. P. - Stability of acrylic polyurethane coatings under accelerated aging tests and natural outdoor exposure: The critical role of the used photo-stabilizers, Progress in Organic Coatings 124 (2018) 137-146. http://dx.doi.org/10.1016/j.porgcoat.2018.08.013
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Vietnam Journal of Sciences and Technology (VJST) is an open access and peer-reviewed journal. All academic publications could be made free to read and downloaded for everyone. In addition, articles are published under term of the Creative Commons Attribution-ShareAlike 4.0 International (CC BY-SA) Licence which permits use, distribution and reproduction in any medium, provided the original work is properly cited & ShareAlike terms followed.
Copyright on any research article published in VJST is retained by the respective author(s), without restrictions. Authors grant VAST Journals System a license to publish the article and identify itself as the original publisher. Upon author(s) by giving permission to VJST either via VJST journal portal or other channel to publish their research work in VJST agrees to all the terms and conditions of https://creativecommons.org/licenses/by-sa/4.0/ License and terms & condition set by VJST.
Authors have the responsibility of to secure all necessary copyright permissions for the use of 3rd-party materials in their manuscript.
Vietnam Journal of Science and Technology (VJST) is pleased to notice: