ELECTRODEPOSITION OF CO-DOPED HYDROXYAPATITE COATING ON 316L STAINLESS STEEL
Keywords:316L stainless steel, Electrodeposition, MgSrFNaHAp
AbstractHydroxyapatite (HAp) co-doped by magnesium (Mg), strontium (Sr), sodium (Na) and fluorine (F) were deposited on the 316L stainless steel (316L SS) substrate by electrodeposition method. The influences of scanning potential ranges, scanning times, scanning rates to form MgSrFNaHAp coating were investigated. The analytical results FTIR, SEM, Xray, EDX, thickness and adhension of the obtained coating at scanning potential ranges of 0 ÷ -1.7 V/SCE; scaning times of 5, scanning rate of 5 mV/s showed that MgSrFNaHAp coatings were single phase crystals of HAp, rod shape with the thickness 8.9 µm and the adhesion strength reached 8.38 MPa.
Authors who publish with Vietnam Journal of Science and Technology agree with the following terms:
- The manuscript is not under consideration for publication elsewhere. When a manuscript is accepted for publication, the author agrees to automatic transfer of the copyright to the editorial office.
- The manuscript should not be published elsewhere in any language without the consent of the copyright holders. Authors have the right to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal’s published version of their work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are encouraged to post their work online (e.g., in institutional repositories or on their websites) prior to or during the submission process, as it can lead to productive exchanges or/and greater number of citation to the to-be-published work (See The Effect of Open Access).