Nghiên cứu điện cực anot trơ hỗn hợp oxit kim loại cho bảo vệ catot chống ăn mòn vỏ tàu biển
Author affiliations
DOI:
https://doi.org/10.15625/2525-2321.2017-00478Keywords:
Mixed metal anode MMO, cathodic protection by impressed current, corrosion of ship hull, current densityAbstract
The corrosion of metals ship hull occurs when it contacts with an marine environment and causes risk and great losses from the economic point of view. The research of using mixed metal anodes (MMO) for ship hull cathodic protection by impressed current has been carried out. The influence of various factors such as: anode current density, salt concentration and flow rate of solution on anode stablity has been examined. It was found that the anode MMO Ti/IrO2/RuO2IrO2TiO2 coud be used at high current density up to 600 A/m2 in 3.5 % NaCl solution and the anode stability decreased in solution of low concentration 0.2 % NaCl. The flow rate of solution has not almost influence on anode stability.
Keywords. Mixed metal anode MMO, cathodic protection by impressed current, corrosion of ship hull, current density.
Downloads
References
Lazzari L., Pedeferri P. Cathodic Protection, 1st Edision (2006).
Corrosion protection of floating production and storage units, Recommended practice DNV-RP-B101.
Automatic systems for ships hulls, MG Duff International Ltd.
Kroon D. H, Ernes L. M. MMO coated titanium anodes for cathodic protection - Part 1, Materials Performance, 45(5), 26-29 (2007).
L. Xu. Impressed current anode for ship hull protection, Materials Performance, 5(6), 40-42 (2011).
V. V. Panic, B. Z. Nikolic. Sol-gel prepared active ternary oxide coating on titanium in cathodic protection, J. Serb. Chem. Soc., 72, 1393-1402 (2007).
Nguyễn Ngọc Phong, Đỗ Chí Linh, Phạm Hồng Hạnh, Ngô Ánh Tuyết. Oxi hoá điện hoá của phenol trên điện cực trơ Ti/RuO2IrO2TiO2 trong môi trường kiềm, Tạp chí Hóa học, 47, 226-229 (2009).
Nguyễn Ngoc Phong. Nghiên cứu chế tạo điện cực anốt trơ titan phủ hỗn hợp ôxit kim loại, Tạp chí Khoa học và Công nghệ, 41, 30-35 (2003).