PHẢN ỨNG GHÉP GLYCIDYLMETACRYLAT LÊN POLYETYLEN PHẦN I. ẢNH HƯỞNG CỦA CÁC YẾU TỐ CÔNG NGHỆ ĐẾN PHẢN ỨNG GHÉP

Abstract

Grafting reactions of glycidylmethacrylate on polyethylene were carried out in a Brabender internal mixer with capacity of 50 ml. There are strong and sharp peak in the PE-g-GMA IR spectra at about 1730 cm^-1corresponding to carbonyl group (C=O) and at 850 và 910 cm^-1corresponding epoxy group, but these peaks have not seen in neat PE spectra. The parameters of process condition were selected to achieve the highest grafting content: the temperature at 185^oC, rotor speed of 40 rpm for 11 min. The received PE-g-GMA possessed: grafting content 1.705 wt.%, melt flow index 5.27 g/10 min and contact angle  45.21^o.