Nghiên cứu ảnh hưởng của tỷ lệ các hợp phần đến phản ứng khâu mạch nhựa epoxy biến tính dầu ve bằng dianhydrit piromelitic
Author affiliations
DOI:
https://doi.org/10.15625/0866-7144.2017-00427Keywords:
Epoxy resin, castor oil, dianhydrite piromelitic, curingAbstract
The influence of the content of epoxy resin modified by castor oil (ECO), dianhydrite piromelitic (PMDA) and dimetylbenzylamin (DMBA) on the crosslinking reaction of ECO by PMDA have been studied and the optimal conditions for the curing have been determined. It was showed that at the optimal conditions: The mol ratio of anhydrite/epoxy = 1.3, reaction temperature 120 oC, the DMBA content of 2.3 % of the total mass of ECO and PMDA, the epoxy and anhydrite groups had been totally converted after 60 min of reaction. The mol ratio of anhydrite/epoxy = 1.3 have been determined to be optimal condition for formation of the cured coating having gel fraction, swelling degree, flexibility, adhesion, impact resistance and relative hardness of 93 %; 150 %; 1 mm, 1 point, 200 kG.cm, and 0.88, respectively.
Keywords. Epoxy resin, castor oil, dianhydrite piromelitic, curing.Downloads
References
Lê Xuân Hiền. Biến đổi hóa học dầu thực vật và ứng dụng, Nxb. Khoa học tự nhiên và Công nghệ, Hà Nội (2013).
Soo-Jin Park, Fan Long Jin. Thermal stabilities and dynamic machanical properties of sulfone-containing epoxy resin cured with anhydride, Polymer Degradation and Stabilitty, 86, 515-520 (2004).
My Phuong Pham. Theoretical studied of mechanisms of epoxy curing systems, The University of Utah, USA (2001).
Jen Rock, Friendrich Vohwinkel, L. Rintoul, Fraeme A. George. The kinetics and mechanism of cure of an amino-glicydyl epoxy resin by a co-anhydride as studied by FT-Raman spectroscopy, Polymer, 45, 6799-6811 (2004).
Brian J. Rohde, Megan L. Robertson, Ramanan Krishnamoorti. Concurrent curing kinetics of an anhydride-cured epoxy resin and polydicyclopentadiene, Polymer, 69, 204-214 (2015).
Lê Xuân Hiền. Báo cáo tổng kết Dự án sản xuất thử nghiệm cấp Viện Hàn lâm KH&CN Việt Nam giai đoạn 2012-2013. Hoàn thiện công nghệ chế tạo sơn cách điện cấp F trên cơ sở nhựa epoxy biến tính dầu thực vật, Hà Nội (2014).
A. Ručigaj, B. Alič, M. Krajnc, U. Šebenik. Investigation of cure kinetics in a system with reactant evaporation: Epoxidized soybean oil and maleic anhydride case study, European Polymer Journal, 52, 105-116 (2014).
Lê Xuân Hiền, Đỗ Thị Ngọc Mai. Nghiên cứu ảnh hưởng của tỷ lệ các hợp phần đến phản ứng khâu mạch nhựa epoxy biến tính dầu đậu nành bằng dianhydrit piromelitic, Tạp chí Hóa học, 52(1), 107-111 (2014).
Lê Xuân Hiền, Đỗ Thị Ngọc Mai. Nghiên cứu ảnh hưởng của nhiệt độ đến phản ứng khâu mạch nhựa epoxy biến tính dầu đậu nành bằng dianhydrit piromelitic và tính chất của màng khâu mạch, Tạp chí Hóa học, 52(3), 312-315 (2014).
Tiêu chuẩn ASTM D 2857-95.