Nghiên cứu ảnh hưởng của nanosilica đến tính chất cơ học của màng polyme polyurea trên cơ sở polyaspartic este desmophen NH1520 đóng rắn bằng Desmodur N3600

Huỳnh Lê Huy Cường, Trần Vĩnh Diệu, Nguyễn Đắc Thành, Đoàn Thị Yến Oanh
Author affiliations

Authors

  • Huỳnh Lê Huy Cường
  • Trần Vĩnh Diệu
  • Nguyễn Đắc Thành
  • Đoàn Thị Yến Oanh

DOI:

https://doi.org/10.15625/0866-7144.2016-00309

Keywords:

Polyurea resin, polyaspartic ester resin Desmophen NH1520, silica nanoparticles, nanosilica, modified nanosilica

Abstract

The effects of silica nanoparticles (nanosilica) to mechanical properties of polymer coating film polyurea based on polyaspartic ester resin Desmophen NH1520 and hardener Desmodur N3600 have been studied. Surface modification of nanosilica was realized by 3-amino propyl triethoxy silan (APTES). Dispersions of nanosilica in polyaspartic ester resin Desmophen NH1520 were carried out by stirring and ultrasonic vibration. The structures of the hybrids were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The thermal properties were characterized by thermo gravimetric analysis (TGA). The results show that nanosilica is good  dispersed and improved mechanical properties of polymer coating film polyurea based on polyaspartic ester resin Desmophen NH1520.

Keywords. Polyurea resin, polyaspartic ester resin Desmophen NH1520,  silica nanoparticles, nanosilica, modified nanosilica.

Downloads

Download data is not yet available.

Downloads

Published

18-07-2016

How to Cite

Huy Cường, H. L., Diệu, T. V., Thành, N. Đắc, & Yến Oanh, Đoàn T. (2016). Nghiên cứu ảnh hưởng của nanosilica đến tính chất cơ học của màng polyme polyurea trên cơ sở polyaspartic este desmophen NH1520 đóng rắn bằng Desmodur N3600. Vietnam Journal of Chemistry, 54(3), 302. https://doi.org/10.15625/0866-7144.2016-00309

Issue

Vol. 54 No. 3 (2016)

Section

Articles