AGING OF WATERBORNE PAINT BASED ON THE ACRYLIC RESIN EMULSION AND ORGANIC PIGMENT
Keywords:Acrylic emulsion, organic pigment, TiO2, water based paint, architectural paint
Aging of waterborne paint on the base of acrylic resin emulsion with and without green Luconyl have been investigated by general appearance assessment, adhesion change, FT-IR and discoloration. The obtained results showed that the both of paint-formulas coatings had no cracks, blisters, flacks and there was no change of adhesion during the aging process. However, IR analysis indicated that there were some changes in chemical structures of coating with and without Green Luconyl during aging process. To specify, IR spectrums of initial and aged coating no containing Green Luconyl illustrated aging process led content of O-H and C=C increased significantly but baseline of spectra was fairly unchanged. For coating filled Green Luconyl, IR spectrums’ shape was fairly stable but baseline saw a clear reduce during accelerated weather exposure. Moreover, SEM images indicated that surfaces morphology of samples changed differently depending on in presence of organic pigment. Surface of aged coating without Luconyl saw rougher than surface of coating with Luconyl after aging process. Hence, the weather aging test had more significant influence on paint coating in absence of Luconyl than paint coating in presence of Luconyl. It was explained that the macroradical produced in aging process would attack into conjugated double bonds of Luconyl instead of double bonds of AC-261 leading to aged coating filled Luconyl become more opaque than initial while coating no filled Luconyl had significant changes in chemical structure during aging process. Although this was a hypothesis, it saw a suitable with the obtained results. The paint coating in presence of Luconyl illustrated significant color change, especially, showed the loss of green color while the other paint coating showed slight color change.
Jablowsky E., Learner T., Hayes J., Golden M.-Conservation concerns for acrylic emulsion paints-Reviews in Conservation, 4 (2003), 3-12.
Le Xuan Hien, Nguyen Thien Vuong, Nguyen Thi Viet Trieu-Study of the humid heat, ultraviolet radiation durability of some coatings based on acrylic resin.I. Study of the influence of chemical natural on humid heat, ultraviolet radiation durability of some coatings based on acrylic resin – Vietnam Journal of Science and Technology, 47 (6) (2009), 69-75.
Le Xuan Hien, Nguyen Thien Vuong, Nguyen Thi Viet Trieu-Study of the humid heat, ultraviolet radiation durability of some coatings based on acrylic resin.II. Study of the influence of natural and content of photo-stabilizer system on humid heat, ultraviolet radiation durability of some coatings based on acrylic polyol HSU 1168 curing with polyisocyante Desmodur N-75 – Vietnam Journal of Chemistry, 47 (6) (2009), 663-667.
Koleske J.V. -Paint and Coating Testing Manual: Fourteenth edition of the Gardner-Sward Handbook-Philadelphia (1995).
Schulz U.-Accelerated testing, Hannover: Vincentz Network-Germany (2009).
Nguyen Thien Vuong-Study of weathering durability of some coatings based on acrylic resins –Doctoral Thesis of Chemistry, Institute for Tropical Technology (2012).
Nguyen Thien Vuong, Dao Phi Hung, Nguyen Anh Hiep, Mac Van Phuc, Trinh Van Thanh, Dinh Thi Lien, The degradation of Primal AC-261 Acrylic emulsion coating in the accelerated weathering test – Vietnam Journal of Chemistry, 53 (2015), 171-179.
Vu Dinh Cu- Fundamental Tropical Technology- Vietnam Culture and Information Publishing House, Ha Noi (2003)
Decker C. –Effect of UV Radiation on Polymer-Handbook of Polymer Science and Technology, 3 (1989), 541-604.
Hu J., Li X., Gao J., Zhao Q.-Ageing behavior of acrylic polyurethane varnish coating in accelerated weathering environments-Progress in Organic Coatings, 65 (2009), 504-509.
Kozak A.-Multi-criteria assessment of an acrylic coating exposed to natural and accelerated weathering-Procedia Engineering, 108 (2015), 664 – 672.
Di Crescenzo M. M., Zendri E., Sánchez-Pons M., Fuster-López L., Dolores Julia Yusá-Marco-The use of waterborne paints in contemporary murals: Comparing the stability of vinyl, acrylic and styrene-acrylic formulations to outdoor weathering conditions-Polymer Degradation and Stability, 107 (2014), 285-293.
Thien Vuong Nguyen, Phuong Nguyen Tri, Tuan Dung Nguyen, Rachid El Aidani, Van Thanh Trinh, Christian Decker, Accelerated degradation of water borne acrylic nanocomposites used outdoor protective coatings, Polymer Degradation and Stability, 128 (2016), 65-76.
Thien Vuong Nguyen, Tuan Anh Nguyen, Phi Hung Dao, Van Phuc Mac, Anh Hiep Nguyen, Minh Thanh Do and The Huu Nguyen-Effect of rutile Titania dioxide nanoparticles on the mechanical property, thermal stability, weathering resistance and antibacterial property of styrene acrylic polyurethane coating-Adv. Nat. Sci.: Nanosci. Nanotechnol. 7 (2016) 045015 (9pp).
Thien Vuong Nguyen, Phi Hung Dao, Khanh Linh Duong, Quoc Hoan Duong, Quoc Trung Vu, Anh Hiep Nguyen, Van Phuc Mac, Trong Lu Le - Effect of R-TiO2 and ZnO nanoparticles on the UV-shielding efficiency of water-borne acrylic coating -Progress in Organic Coatings 110 (2017) 114–121
Authors who publish with Vietnam Journal of Science and Technology agree with the following terms:
- The manuscript is not under consideration for publication elsewhere. When a manuscript is accepted for publication, the author agrees to automatic transfer of the copyright to the editorial office.
- The manuscript should not be published elsewhere in any language without the consent of the copyright holders. Authors have the right to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal’s published version of their work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are encouraged to post their work online (e.g., in institutional repositories or on their websites) prior to or during the submission process, as it can lead to productive exchanges or/and greater number of citation to the to-be-published work (See The Effect of Open Access).