PHẢN ỨNG GHÉP GLYCIDYLMETACRYLAT LÊN POLYETYLEN PHẦN II. ẢNH HƯỞNG CỦA THÀNH PHẦN HÓA HỌC ĐẾN PHẢN ỨNG GHÉP

Nguyễn Thị Thuỷ, Nguyễn Huy Tùng, Bùi Chương
Author affiliations

Authors

  • Nguyễn Thị Thuỷ
  • Nguyễn Huy Tùng
  • Bùi Chương

DOI:

https://doi.org/10.15625/2109

Abstract

The influence of dicumyl peroxide (DCP), glycidyl methacrylate (GMA) and styrene on the effiency of grafting reaction of GMA on polyethylene (PE) was studied. The results showed at DCP content of 0.5 phr the highest grafting yield was obtained while the MFI and contact angle reached the smallness values. The grafting yield, MFI and contact angle were found to be optimum for the GMA content of 12 phr. The molar ratio styrene with GMA made grafting yield increased from 1.999%wt to 3.354 %wt.

Downloads

Download data is not yet available.

Published

14-08-2012

How to Cite

Thuỷ, N. T., Tùng, N. H., & Chương, B. (2012). PHẢN ỨNG GHÉP GLYCIDYLMETACRYLAT LÊN POLYETYLEN PHẦN II. ẢNH HƯỞNG CỦA THÀNH PHẦN HÓA HỌC ĐẾN PHẢN ỨNG GHÉP. Vietnam Journal of Chemistry, 49(3). https://doi.org/10.15625/2109

Issue

Section

Articles