Nghiên cứu biến tính bề mặt ống cacbon nano bằng phản ứng este hóa Fischer

Đỗ Quang Kháng, Chu Anh Vân, Lê Hồng Hải, Hồ Thị Oanh
Author affiliations

Authors

  • Đỗ Quang Kháng
  • Chu Anh Vân
  • Lê Hồng Hải
  • Hồ Thị Oanh

DOI:

https://doi.org/10.15625/0866-7144.2015-00173

Keywords:

Carbonnanotube, surface modification, TESPT

Abstract

In this work, carbonnanotubes (CNT) was firstly purified to remove residual metal catalyst in the preparation process. Afterward, H2O2/NH3 mixture was used as the oxidizing agent for CNT treatment in order to form functional groups COOH and NH2 on CNT surface. Polyethyleneglycol and bis(3-triethoxysilylpropyl) tetrasulfide (TESPT) were then grafted onto the oxidized surface of CNT under appropriate conditions of Fischer esterification reaction. The structure of CNT and modified CNT were characterized by infrared spectroscopy, Raman, transmission electron microscopy (TEM) and weight thermal analysis (TGA). The results have proven that organic functional groups (-COOH and -NH2) were successfully attached onto the surface of CNT and the content of the organic functional group is about 27.85 %. By the CNT modified with PEG and TESPT the content of –CO-PEG and –CO-TESPT are about 24.66 % and 3.28 %, respectively.

Downloads

Download data is not yet available.

Downloads

Published

31-08-2015

How to Cite

Kháng, Đỗ Q., Vân, C. A., Hải, L. H., & Oanh, H. T. (2015). Nghiên cứu biến tính bề mặt ống cacbon nano bằng phản ứng este hóa Fischer. Vietnam Journal of Chemistry, 53(4), 520–525. https://doi.org/10.15625/0866-7144.2015-00173

Issue

Section

Articles