Tổng hợp vật liệu bằng phương pháp phản ứng nổ và tính chất của LaPO4:Eu kích thước nanomet

Nguyễn Vũ, Phạm Đức Roãn, Tạ Minh Thắng, Trần Thị Kim Chi, Mẫn Hoài Nam, Nguyễn Thị Thanh
Author affiliations

Authors

  • Nguyễn Vũ
  • Phạm Đức Roãn
  • Tạ Minh Thắng
  • Trần Thị Kim Chi
  • Mẫn Hoài Nam
  • Nguyễn Thị Thanh

DOI:

https://doi.org/10.15625/0866-7144.2015-00166

Keywords:

LaPO4, Eu, combustion synthesis, nanomaterials, nanophosphors, luminescent

Abstract

Eu (III)-doped LaPO4 nanophosphors were prepared via combustion synthesis using urea as fuel and metal nitrates as precursor. Structures, morphologies, and photoluminescent properties of the LaPO4:Eu were studied by X-ray diffraction, scanning electron microscopy, photoluminescent and excitation photoluminescent spectra. The average diameters for the phosphor particles are 5-20 nm. The effects of Eu(III) doping process and heating temperature on structure and optical properties of nanophosphors have been investigated. LaPO4:Eu phosphors show the intense peak at 594 nm corresponding to the 5D0-7F1 transition of Eu (III) in inversion symmetry sites.

Downloads

Download data is not yet available.

Downloads

Published

31-08-2015

How to Cite

Vũ, N., Roãn, P. Đức, Thắng, T. M., Kim Chi, T. T., Nam, M. H., & Thanh, N. T. (2015). Tổng hợp vật liệu bằng phương pháp phản ứng nổ và tính chất của LaPO4:Eu kích thước nanomet. Vietnam Journal of Chemistry, 53(4), 480–484. https://doi.org/10.15625/0866-7144.2015-00166

Issue

Section

Articles