Flame retardancy improvement of modified cotton fabric by nano silica sol coating

Pham Thi Thu Trang, Le Ha Giang, Nguyen Ba Manh, Tran Quang Vinh, Trinh Duc Cong, Vu Anh Tuan
Author affiliations

Authors

  • Pham Thi Thu Trang Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam
  • Le Ha Giang Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam
  • Nguyen Ba Manh Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam
  • Tran Quang Vinh Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam
  • Trinh Duc Cong Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam
  • Vu Anh Tuan Institute of Chemistry, VAST, 18 Hoang Quoc Viet, Cau Giay, Ha Noi, Viet Nam

DOI:

https://doi.org/10.15625/2525-2518/58/4/14850

Keywords:

nanosilica, cotton fabric, flame retardancy

Abstract

Cotton fabric was coated by silica sol at different times using dip-coating method. Nano silica coated fabrics were characterized by XRD, FTIR, SEM, EDX, TGA. From SEM result, it showed that fabric surface was coated by nanosilica particles of 20-30 nm size. Nano silica coated fabrics showed the improvement not only flame retardancy (LOI increased from 18.4 to 30.8) but also the tear strength. Tear strength increased from 23 N/mm (cotton fabric) to 29.9 N/mm (fabric coated nanosilica at 3 times).

Downloads

Download data is not yet available.

References

Prof. Thai Hoang

Email: hoangvast@gmail.com

Prof. Do Quang Khang

Email:khangdoquang@gmail.com

Downloads

Published

13-07-2020

How to Cite

[1]
P. T. T. Trang, L. H. Giang, N. B. Manh, T. Q. Vinh, T. D. Cong, and V. A. Tuan, “Flame retardancy improvement of modified cotton fabric by nano silica sol coating”, Vietnam J. Sci. Technol., vol. 58, no. 4, pp. 473–480, Jul. 2020.

Issue

Section

Materials